Description
| Weld Metal Chemical Analysis (%) | |||||
| Flux + Wire | C | Si | Mn | Mo | |
| KJF – 615+ KJS – 124 ( S2Mo ) | 0.04 – 0.06 | 0.25 – 0.35 | 1.65 – 1.9 | 0.40 – 0.50 | |
| Weld Metal Mechanical Properties | |||||||
| Flux + Wire | U.T.S. | Y.T.S. | EL | Charpy test | |||
| ( Mpa) | ( Mpa) | (%) | RT | -30°C | -40°C | -50°C | |
| KJF – 615 + KJS – 124 ( S2Mo ) | 620 – 635 | 540 – 565 | 22 – 24 | 70-90 | 55-75 | 40 – 55 | — |
| Technical Specifications |
| Basicity Index | 1.5 According to Boniszewski formula |
| Density | 1.25 Kg/dm3 |
| Re-drying | 350 ± 25o C /2hr |
| Current | AC / DCEP |
| Packing | 25 Kg bag (3 layers) / other sizes as per buyer’s order |
| Advantages |
Basic Aluminate Agglomerated Flux
Excellent slag detachability even in high temperature with homogenous weld bead without undercut.
Suitable for Spiral and longitudinal welding thick oil and gas pipes up to X80 grade
Outstanding properties in combination with TB content wire in four wires welding (sour gas pipe welding)